TRILITE RMS ( Reinforced Magnesium Silicate ) is the result of our company’s endeavor to offer the construction industry with a highly durable, stable and superior performance board for a wide range of interior and exterior application. Innovatively produce from a mixture of inorganic natural silicates, CaCO3 (Calcium Carbonate), MgCl (Magnesium Chloride), MgO (Magnesium Oxide) and reinforce with glass fiber to form a smooth, flat, highly stable & durable, environmental friendly, noncombustible, 100% asbestos free board.  Our magnesium based board is available in both smooth and rough surface patterns. The rough pattern is ideal for applications wherein the surface will be laminated with tiles, veneers and the likes because it offers better adhesion bonding than the smooth surface.
Dimensions

Fire Resistance
Thickness (mm) Size (mm) Mass ( Kg/ Sheet)
3
 915 x 1830mm
1220 x 2440mm
 9.8 Kg
4 13 Kg
6
 18 Kg
8
 25 Kg
9
 28 Kg
10 31 Kg
12
 35 Kg
15
 44 Kg
18
53 Kg
Standard Testing Authority Test Result
BS 476 part 4, BS EN ISO 1182
 Warrington Fire Research
 Non combustible
BS 476 part 7
Warrington Fire Research Class 1 surface spread of flame
BS 476 part 22 CERAM U.K. 180 mins integrity (single side 12 mm board)
BS 476 part 22 CERAM U.K. 120 mins integrity & insulation (steel stud)
BS 476 part 22 CERAM U.K. 120 mins integrity & insulation (timber stud)
BS EN ISO 1716 BRE U.K. Evolved heat of component parts
BS EN ISO 13501-1 BRE U.K. Non combustible Class ‘A1
more fire resistance specs..
Note : (1) Other dimensions are available on request at a minimum quantity requirement.
  (2) 15mm and 18mm are non standard and produce by request.
  (3) Square Edge and 45° Tapered Edge Boards are available.
 
Dimensional Tolerance (mm)
Thickness -0.2mm , +0.4mm
Width -2mm , + 2mm
Length -2mm , + 3mm
Squareness 5mm
 
Biological Resistance
Rodent Resistance Highly Resistant
Termite Resistance No Damage
Resistance to Bacteria Highly Resistant
Resistance to Mildew Growth No Growth

Freeze/Thaw Test
Frozen at -17.5+ 2.5 continuously for over 16 hours. Kept frozen at -17.5 for 4 hours. Thawed by immersing in water at approximately 20. Maintained at a temperature of 20 ± 3 for 5 hours. Freeze and thaw cycle is repeated 10 times
Test result: No cracking, disintegration, crumbling, stripping occurs on the TRILITE RMS Board and achieve the Freeze/thaw value of 1.97%

Water Endurance Test
No bloating on reverse side. Non-occurrence of swelling, breakage nor tearing apart of the board.

Sound insulation
Sound Reduction Index (Rw)
Frequency (Hz)
 100 125 160 200 250 315 400 500 630 800
Sound Absorption (dB) 16.8 29.5 31.9 25.6 23 33.6 40 40.9 40.2 44.8
Frequency (Hz) 1000 1250 1600 2000 2500 3150 4000 5000 6300 8000
Sound Absorption (dB) 48.5
51.3 52.4 53.7 52.6 43.6 43.2 49.7 55 59.4
*Specimens 9mm on both sides, mineral wool = 93mm partition
*Weighted Sound Reduction Index (Rw): 38dB
Dimensional Stability Mechanical & Physical Properties
Test Item
Unit Test Result
Thickness Swelling
   After 24 Hours Immersion % 0.2%
   After Freeze/ Thaw Test % -0.1%
Moisture Exposure Elongation Rate % <0.9%
Water Absorption % 32%
Heat Exposure Deformation Rate % <0.2%

Downloadables
Material Safety & Data Sheet Product Catalog Test Reports
Test Item Unit Test Result

Density (Average)

Kg/m3 1100 ±100
Bending Strength N/mm2 12.1
Tensile Strength N/mm2 1.97
Impact Strength N/mm2 23
Moisture Content % 9±5
Moisture Exposure Expansion Rate % 0.2
Thermal Conductivity W/mK 0.139
Surface Alklinity pH 9.5-10
Asbestos Check   Not detected